A titanium-based platinum electrode is a special electroplating process. Platinum is plated on the surface of a specially treated titanium substrate, which can be fully or partially plated or even plated on composite materials such as titanium-clad copper. The product surface is silver white, with the advantages of uniform and fine coating, firm combination, large output current, long service life, etc. Mainly used in electroplating, biomedical, chemical synthesis, cathodic protection, and other fields
Base material: Grade I pure titanium TA1 GR1
Working current range: ＜ 15000A/㎡
Operating temperature: ＜ 85 ℃
Plating metal: 99.99% Pt
Platinum content: 22.45g/m2/ μ m
Platinum layer thickness: 0.1-15 μ m
Product shape: net, plate, tube, rod, etc
Operating environment: PH value: 0-14
Instructions for use: prevent hard objects from scratching, take them out of the electrolytic cell when they are not in use, wash the surface with clean water, and store them dry. The greater the current, the shorter the service life. If the solution containing fluoride ions is used, the electrode will be quickly damaged.
Platinum titanium electrode is coated at high temperatures. Various shapes, platinum content of 12g/m2/ μ m. Platinum layer thickness 0.2-5 μ m。 It is mainly used for local conductive contact of titanium electrode plates under high current environments (such as steel plate galvanizing, PS plate, etc.), and preparation of acid and alkaline ionized water.
Base material: titanium (Gr1, Gr2, TA1, TA2)
Shape: plate, bar (customized), profile
Current density: ＜ 8000 A/m2
Manufacturing process: electroplating
Coating material: platinum (99.99% purity)
Precious metal content: ≥ 21.48 g/㎡
Platinum layer thickness: 0.2-15 μ m
Temperature: ＜ 80 ℃
PH value: 1-12
Technical features: The platinum layer is firmly combined with a titanium base substrate, with stable performance, high current, and low voltage. It is used for precious metal plating baths, and the coating is even
Application: seawater, potassium gold cyanide+citric acid, horizontal electroplating, pulse electroplating, cathodic protection, acidic and alkaline electroplating solutions.